Hadfield High Manganese Steel Plates Suppliers

 Hadfield High Manganese Steel Plates Widely known for its mix making properties, are shocking to high-affect wear applications or those in which scratch scratched spot is experienced. These set steel plates update in a general sense on various events the hardness of smooth steel and flawless around different events the hardness of proceeded with tempered steel. Hence, one can respect a suitably drawn out future and expanded security of their contraption and working environments.

Hadfield High Manganese steel for security from veritable effect and beating wear. It is mix making steel. WORK HARDENING embraces the course by which that the steel bends up steadily hard the more it is affected or squeezed.Hadfield High Manganese steel for security from veritable effect and beating wear. It is mix making steel. WORK HARDENING embraces the course by which that the steel bends up steadily hard the more it is affected or squeezed.

The "Hadfield" grade has a stand-out hardness of around 220 Brinell. With proceeded with effect or potentially weight it will surface concrete to more than 550 Brinell.It ought to be seen that just the outside skin surface bonds. The under layer remains astoundingly flexible and silly. As the surface wears, it reliably connects with itself seeing the opportunity to be always hard.

Features Provided

•  High strength, Sturdiness
•  Durability
•  High Abrasion Resistance
•  Non-Magnetic Properties
•  Deep Uniform Hardness
•  Provide Maximum Wear Life
•  Excellent Toughness

Technical Specification

• Tensile - 132,000 PSI
• Hardness - 250BHN
• Yield - 90,000 PSI
• Will Work Hardened to 500BHN
• Elongation - 12%

Chemical Analysis Typical values (% weight)

C	Si	Mn	S	P
1.13	0.40	13	0.003	≤ 0.20

Mechanical Properties

	Hardness HB	Yield Strength MPa	UTS MPa	El%	KCV 20�C (68�F) - J
Typical Values	220	380(55 KSI)	940(136 KSI)	40	≥ 112 J(≥ 83 ft.lbs)
Guaranteed Values*	180/245	350(51 KSI)	800(116 KSI)	30	64 J(47 ft.lbs)

Physical Properties

	Density *	Expansion Coeff. 0-600�C	Specific Heat	Electrical * Resistivity	Thermal * Conductivity	Magnetic * Permeability
Metric US	7.88	10 -6�C1  21.5  10 -60�F-1 19.9	J/Metric Kg. �C  502  BTU/lb�F  .12	�O.m 75 �O.m 75	W/m. �C  13 BTU/hr.ft�F 7.3	�1.002

Advantages

•  Resistance to high abrasion and severe impact.
•  Will work hardened rapidly to 550BHN.
•  Remains ductile throughout.
•  Hadfield Grade, Can be welded.
•  Has non-magnetic properties.
•  Can be cut with oxy-acetylene torch, plasma, water jet, or laser.
•  Made to the toughest standards in the industry for extended service life

Applications

•  Quarries and constructions
•  Mines
•  Iron industry and foundry
•  Concrete and brick works
•  Scraps
•  Automotive industries
•  Impact mills
•  Centrifugal mills
•  Protective grills